Abstract
Biaxial stress is identified to play an important role in the polar orthorhombic phase stability in hafnium oxide-based ferroelectric thin films. However, the stress state during various stages of wake-up has not yet been quantified. In this work, the stress evolution with field cycling in hafnium zirconium oxide capacitors is evaluated. The remanent polarization of a 20 nm thick hafnium zirconium oxide thin film increases from 9.80 to 15.0 µC cm−2 following 106 field cycles. This increase in remanent polarization is accompanied by a decrease in relative permittivity that indicates that a phase transformation has occurred. The presence of a phase transformation is supported by nano-Fourier transform infrared spectroscopy measurements and scanning transmission electron microscopy that show an increase in ferroelectric phase content following wake-up. The stress of individual devices field cycled between pristine and 106 cycles is quantified using the sin2(ψ) technique, and the biaxial stress is observed to decrease from 4.3 ± 0.2 to 3.2 ± 0.3 GPa. The decrease in stress is attributed, in part, to a phase transformation from the antipolar Pbca phase to the ferroelectric Pca21 phase. This work provides new insight into the mechanisms controlling and/or accompanying polarization wake-up in hafnium oxide-based ferroelectrics.