Abstract
This report covers the activities associated with the development and evaluation of two high-’ superalloys that were designed by external partners on this project, namely Carpenter Technologies Corporation and the University of California-Santa Barbra. One alloy was GammaPrint-700, a cobalt-base superalloy, and the other a nickel-base (Ni-base) superalloy GammaPrint-1100. Both were found to be printable through laser powder bed fusion (LPBF) additive manufacturing, with optimal process parameter sets being identified for each alloy. Further, high temperature mechanical testing was conducted on each alloy that showed both materials performed better than the comparative baseline (LPBF Hastelloy X), with the Ni-base superalloy being down-selected for scaling and printing of the tip shoe components.